Metallized mylar Film with plasma Treated on line

Metallized Bopet film with plasma treated,
Before metallising ,the clear film passed through the plasma treated,then metallising on the opposite side with plasma treated for improving the adhesive ability and wetting tension on this side.Wetting tension on both sides is above 56dyne/cm.

  • Hongrun
  • Made in China
  • 2-4weeks from the PO date
  • 500tons/month
  • Information

Metallising the Polyester film with plasma treated on line,

Thickness: 8mic-125mic

Optical density: 0.25-3.5

Wetting tension on both sides is above 54dyne.The metallized PET film with plasma treated improved the adhesive ability on metal side,and mainly used for flexible packing without retortable ability.

Technical date sheet:

Specification

HO-104

Test Date


Test temperature

23℃

Thickness

12mic

Test Item

Unit

Test Standard

Test Result

Test Method

Tensile

MD

M pa

≥170

225

ASTM D-882

TD

≥170

211

Elongation at break

MD

%

≥80

126

ASTM D-882

TD

≥80

122

Shrinkage

(150℃30min)

MD

%

 ≤2.5

1.45

 

ASTM D-1204

TD

≤1

0.01

Haze

TD

%

≤3.5

2.7

ASTM D-1003

Metallization Adhesion

N

≥1.4/15mm

2.2

3M

Metallization Evenness

%

±10

5.1

Macbeth TD904

Thickness of Aluminum Layer

 Optical density

≥ 2.0

2.22

Wetting Tension on corona side

Dyne/cm

≥52

58

ASTMD-2578

Appearance

Qualified

Test Conclution

Qualified


Get the latest price? We'll respond as soon as possible(within 12 hours)
This field is required
This field is required
Required and valid email address
This field is required
This field is required