Metallized Polyester Film with plasma Treated on line
Metallized Bopet film with plasma treated,
Before metallising ,the clear film passed through the plasma treated,then metallising on the opposite side with plasma treated for improving the adhesive ability and wetting tension on this side.Wetting tension on both sides is above 56dyne/cm.
- Hongrun
- Made in China
- 2-4weeks from the PO date
- 500tons/month
- Information
Metallising the Polyester film with plasma treated on line,
Thickness: 8mic-125mic
Optical density: 0.25-3.5
Wetting tension on both sides is above 54dyne.The metallized PET film with plasma treated improved the adhesive ability on metal side,and mainly used for flexible packing without retortable ability.
Technical date sheet：
Specification | HO-104 | Test Date | |||
Test temperature | 23℃ | Thickness | 12mic | ||
Test Item | Unit | Test Standard | Test Result | Test Method | |
Tensile | MD | M pa | ≥170 | 225 | ASTM D-882 |
TD | ≥170 | 211 | |||
Elongation at break | MD | % | ≥80 | 126 | ASTM D-882 |
TD | ≥80 | 122 | |||
Shrinkage (150℃30min) | MD | % | ≤2.5 | 1.45 |
ASTM D-1204 |
TD | ≤1 | 0.01 | |||
Haze | TD | % | ≤3.5 | 2.7 | ASTM D-1003 |
Metallization Adhesion | N | ≥1.4/15mm | 2.2 | 3M | |
Metallization Evenness | % | ±10 | 5.1 | Macbeth TD904 | |
Thickness of Aluminum Layer | Optical density | ≥ 2.0 | 2.22 | ||
Wetting Tension on corona side | Dyne/cm | ≥52 | 58 | ASTMD-2578 | |
Appearance | Qualified | ||||
Test Conclution | Qualified | ||||